Oxidation‐led decomposition of hexagonal boron nitride coatings on alloy substrates at 900°C: Ti‐6Al‐4V
Christopher Fleming
Design, Manufacturing And Engineering Management
Research output
:
Contribution to journal
›
Article
›
peer-review
1
Citation (Scopus)
54
Downloads (Pure)
Overview
Fingerprint
Datasets
(1)
Fingerprint
Dive into the research topics of 'Oxidation‐led decomposition of hexagonal boron nitride coatings on alloy substrates at 900°C: Ti‐6Al‐4V'. Together they form a unique fingerprint.
Sort by
Weight
Alphabetically
Engineering
Substrates
100%
Boron
100%
Nitride
100%
Coating
100%
Alloy
100%
Oxidation Reaction
44%
Crystallite
11%
Solute
11%
Titanium
11%
Solid Solution
11%
Mechanisms
11%
Basal Plane
11%
Periphery
11%
Diffusion Barrier
11%
Chemistry
Coating Agent
100%
Alloy
100%
Aluminum
100%
Decomposition
100%
Rutile
33%
Oxidation Reaction
22%
Titanium
22%
Ion
22%
Boron Atom
22%
Borate
22%
Oxide
11%
Reaction Mechanism
11%
Nitrogen
11%
Isolation Method
11%
Ceramic
11%
Crystallite
11%
Solid Solution
11%
Solute
11%
Material Science
Boron Nitride
100%
Coating
100%
Alloy
100%
Borate
22%
Solid Solution
11%
Crystallite
11%
Aluminum Oxide
11%
Powder
11%
Ceramic Material
11%
Air
11%
Oxide
11%
Material
11%
Ceramics
11%