Behaviour and constitutive modelling of ductile damage of Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si alloy under hot tensile deformation

Junling Li, Baoyu Wang, He Huang, Shuang Fang, Ping Chen, Jie Zhao, Yi Qin

Research output: Contribution to journalArticle

3 Citations (Scopus)
2 Downloads (Pure)

Abstract

In this paper, the flow softening and ductile damage of TC6 alloy were investigated using a uniaxial hot tensile test with deformation temperatures of 910 °C∼970 °C and strain rates of 0.01 s−1∼10 s−1. Scanning electron microscopy (SEM) was performed on the deformed specimens to reveal the damage mechanism. The results showed that the flow stress rapidly increases to a peak at a tiny strain, followed by a significant decrease due to flow softening and ductile damage. The ductile damage of the studied TC6 alloy can be ascribe to the nucleation, growth and coalescence of microdefects, and the microvoids preferentially nucleate at the interface of the alpha phase and beta matrix due to the inconsistent strain. Then, a set of unified viscoplastic constitutive equations including flow softening and ductile damage mechanisms was developed and determined, and this set of equations was verified by the experimental flow stress, which indicated the reliability of the prediction. Furthermore, the predicted normalized dislocation density and the adiabatic temperature rise increase with decreasing temperature and increasing strain rate. The predicted damage components show that the microdefects mainly nucleate in the initial stage, but then primarily grow and link together with continuing deformation.
Original languageEnglish
Pages (from-to)284-292
Number of pages9
JournalJournal of Alloys and Compounds
Volume780
Early online date28 Nov 2018
DOIs
Publication statusPublished - 5 Apr 2019

    Fingerprint

Keywords

  • ductile damage
  • flow behaviour
  • titanium alloy
  • unified constitutive model
  • micro defects
  • nucleation

Cite this